DIN1.2210 Tool Steel Bar Round Metal Bar Hot Forged Blade Silver Cold Work

SHANGHAI UNITE STEEL

DIN1.2210 Tool Steel Bar Round Metal Bar Hot Forged Blade Silver Cold Work

  • 1
  • 2

Brand Name : UST

Model Number : 1.2210

Certification : ISO 9001:2008

Place of Origin : CHINA

MOQ : 1-3 Ton/Tons

Payment Terms : L/C, T/T

Supply Ability : 1000 Ton/Tons per Month

Delivery Time : 5-8 work days

Packaging Details : tool steel sea-worthy packing

Delivery Condition : Annealed , Quenched + Tempered

Similar Grade : DIN1.2210, 115CRV3, L2, SKS43

Shape : Round, Flat, Square.

Surface Condition : Black, Grinded, Rough Turned, Milled, Polished

Contact Now

W. NR. DIN 1.2210 Hot Forged Blade Silver Cold Work Tool Steel Metal Round Bar Rod

DIN1.2210 Hot forged Tool Steel Bar

Similar Grade: DIN1.2210, 115CRV3, L2, SKS43

Shape: Round, Flat, Square.

Size Range:

Diameter(mm) Thickness (mm) Width (mm) Length(mm)
Round 65-420 - - 2000-5800
Square 50-420 - - 2000-5800
flat - 20-100 100-600 2000-5800

Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished

Features:
1. Competitive price
2. Immediate delivery
3. Premium quality
4. Reliable service
5. MOQ: 1 Ton

Packing details In seaworthy packing, as your requirement.
Delivery details within 30-50 days

Chemical Composition:

Grade C Mn P S Si Cr Mo V
1.2210

1.10-

1.25

0.20-

0.40

0.030 0.030

0.15-

0.30

0.50-

0.80

-

0.07-

0.12

Mechanical Properties:

Chromium-vanadium alloyed cold work tool steel with high wear resistance, high edge holding properties, simple heat treatment, good machinability and toughness properties, bright ground and polished according to standard DIN 670 h8.

Density: at 20 °C 7,80 kg/dm3 Thermal expansion between : 20 °C and... °C, 10-6 m/(mK)

Thermal conductivity: at 20 °C 32,0 W/(m.K)

100ºC 200ºC 300ºC 400ºC 500ºC
11.8 12.5 12.9 13.5 13.7

Heat Treatment:

Annealing: 710 - 750 °C

Hardness after annealing: Max. 220 HB

Stress relieving: Approx. 650 °C

Hot forming: 1050 - 850 °C

Hardening: 780 - 810 °C or 810 - 840 °C

Quenching media: 780 - 810 °C, Water 810 - 840 °C, Oil ( up to 15 mm diameter )

Hardness after quenching: 64 - 66 HRC

Applications:

Silver steel for guiding pins, small tools and structural parts in precision mechanics, button-type drills and jagged bits,

screw taps, milling cutters, broaching tools, piercing punches, ejector pins, twist drills, punches and taps, surgical instruments,

reamers, countersinks, dowels, engraving tools, metal cutting saws, axles and shafts, toothed drills, scraping

tools, gear cutters, mortice, wood chisels, guide rods.

Product Introduction:

Al-alloyed nitriding steel grade for large-sections.


Product Tags:

tool steel rod

      

tool steel round bar

      
China DIN1.2210 Tool Steel Bar Round Metal Bar Hot Forged Blade Silver Cold Work wholesale

DIN1.2210 Tool Steel Bar Round Metal Bar Hot Forged Blade Silver Cold Work Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: SHANGHAI UNITE STEEL
*Subject:
*Message:
Characters Remaining: (0/3000)
 

Friendly Links: www.everychina.com

Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Help

Copyright © 2009 - 2024 frbiz.com. All rights reserved.